PE 66011-2
| Properties | Standard method | Unit | Value |
|---|
| Alappolimerek sűrűsége | ISO 1183 | g/cm3 | 0,919-0,921 |
| Alappolimerek MFI (2,16 kg/190 °C) | ISO 1133 | g/10 min | 18,00-22,00 |
| Térfogat | - | g/cm3 | 700-900 |
| Fényállóság (L) | DIN 54001 | - | 8 |
| Hőállóság (T) | DIN 53388 | °C | 280 |
| * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. | MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. | MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. | MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. |