Ezüst
Egyetlen találat van
-
PE 2000
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 8 Hőállóság (T) DIN 53388 °C 300 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 20005
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7-8 Hőállóság (T) DIN 53388 °C 280 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 20020
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 8 Hőállóság (T) DIN 53388 °C 300 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm.