Zöld
Megjelenítve 11–19-ig, az összesen 19 találatból
-
PE 5072
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7 Hőállóság (T) DIN 53388 °C 240 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 5081
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7 Hőállóság (T) DIN 53388 °C 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 5200
Properties Standard method Unit Value Base polymer Density ISO 1183 g/cm3 0,919-0,921 Base polymer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 12,0-16,0 Density - g/dm3 1300 Light resistance (L) DIN 53388 - 7-8 Heat resistance (T) DIN 53772 Celsius 260 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm.
A részletes termékleírás itt letölthető. -
PE 56551
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7-8 Hőállóság (T) DIN 53388 °C 260 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm.
A részletes termékleírás itt letölthető. -
PE 56600
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7-8 Hőállóság (T) DIN 53388 °C 260 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 56603
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7-8 Hőállóság (T) DIN 53388 °C 260 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 56650
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7-8 Hőállóság (T) DIN 53388 °C 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 57702
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7 Hőállóság (T) DIN 53388 °C 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PEM 500
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7 Hőállóság (T) DIN 53388 °C 280 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm.