PE 62004
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 8 Hőállóság (T) DIN 53388 °C 300 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm.
A részletes termékleírás itt letölthető. -
PE 64105
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7 Hőállóság (T) DIN 53388 °C 260 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 64115
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7 Hőállóság (T) DIN 53388 °C 260 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 64119-2
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 8 Hőállóság (T) DIN 53388 °C 280 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 64120
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 8 Hőállóság (T) DIN 53388 °C 280 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 66001
Properties Standard method Unit Value Base polymer Density ISO 1183 g/cm3 0,919-0,921 Base polymer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Bulk Density - g/dm3 600-900 Light resistance (L) DIN 53388 - 8 Heat resistance (T) DIN 53772 Celsius 300 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm.
A részletes termékleírás itt letölthető. -
PE 66011-2
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 8 Hőállóság (T) DIN 53388 °C 280 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 66013
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 8 Hőállóság (T) DIN 53388 °C 280 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 66018
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 8 Hőállóság (T) DIN 53388 °C 300 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm.