PE 4023
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7-8 Hőállóság (T) DIN 53388 °C 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 4049
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 6-7 Hőállóság (T) DIN 53388 °C 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 4057
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 6-7 Hőállóság (T) DIN 53388 °C 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 4070
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 6-7 Hőállóság (T) DIN 53388 °C 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 4085
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7 Hőállóság (T) DIN 53388 °C 20 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 4091
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7 Hőállóság (T) DIN 53388 °C 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 4092
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7 Hőállóság (T) DIN 53388 °C 260 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 4094
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7 Hőállóság (T) DIN 53388 °C 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 41865
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogatsúly - g/cm3 700-900 Fényállóság (L) DIN 54001 - 6-7 Hőállóság (T) DIN 53388 °C 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm.