PE 4037
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7 Hőállóság (T) DIN 53388 °C 260 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 4053
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7 Hőállóság (T) DIN 53388 °C 260 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 4054
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 8 Hőállóság (T) DIN 53388 °C 300 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 4058
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7-8 Hőállóság (T) DIN 53388 °C 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 4084
Tulajdonságok Mérési módszer Mérték egység Érték Alappolimer sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 7 Hőállóság (T) DIN 53388 °C 260 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 4087
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/cm3 700-900 Fényállóság (L) DIN 54001 - 8 Hőállóság (T) DIN 53388 °C 300 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. -
PE 4800
Properties Standard method Unit Value Base polymer Density ISO 1183 g/cm3 0,919-0,921 Base polymer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Bulk Density - g/dm3 600-900 Light resistance (L) DIN 53388 - 7 Heat resistance (T) DIN 53772 Celsius 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm.
A részletes termékleírás itt letölthető. -
PE 4801
Properties Standard method Unit Value Base polymer Density ISO 1183 g/cm3 0,919-0,921 Base polymer MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Bulk Density - g/dm3 600-900 Light resistance (L) DIN 53388 - 7 Heat resistance (T) DIN 53772 Celsius 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm.
A részletes termékleírás itt letölthető. -
PE 4904
Properties Standard method Unit Value Alappolimerek sűrűsége ISO 1183 g/cm3 0,919-0,921 Alappolimerek MFI (2,16 kg/190 °C) ISO 1133 g/10 min 18,00-22,00 Térfogat - g/dm3 700-900 Fényállóság (L) DIN 53388 - 6-7 Hőállóság (T) DIN 53772 Celsius 230 * MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm. MFI measured at 190°C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm.